MICRO-ALLOYED, FINE-GRAINED, THERMO-MECHANICALLY ROLLED HIGH STRENGTH STEEL FOR COLD FORMING.
S700MC combines a minimum yield strength of 700 MPa with high tensile strength and good impact toughness.
The high yield strength enables improved load bearing capacity in combination with weight reduction of components and/or structures.
The use of S700MC opens possibilities for advanced, innovative design with reduced steel thickness.
S700MC offers excellent cold forming properties and weldability. Overall processing becomes easy and efficient.
Reduced steel thickness translates immediately into increased payload and savings on fuel consumption.
Many applications in the (heavy) transport sector may enjoy the economic benefits.
The upgrade from lower yield strength steels to S700MC supports you in your ambitions to reduce CO2 footprint.
Chemical composition (EN 10149-2)
|% min.||-||-||-||-||-||≥ 0,015||-||-||-||-||-|
|≤ 2,10||≤ 0,60 1||
|1 If hot-dip-galvanizing is required, please check the specific Si-content vbefore placing your order.|
Mechanical properties (EN 10149-2)
|Yield strength||Tensile strength||Elongation||Bending radius2|
|ReH (MPa) 1||Rm (MPa) 1||A50 (%) 1||(90°) 2|
|min.||700||750||12||2,0 3 - 2,5 4 x t|
1 tested in longitudinal direction 2 in transversie direction 3 thickness 3 < t < 6 mm 4 thickness t > 6 mm.
EN 10149-2 does not prescribe any minimum impact strength values. However, > 40 J at -20 °C or > 27 J at -40 °C are quite common.
Please express your wish when requiring a quote.
Thickness, width, length, shape and flatness acoording to EN 10051.
Tighter tolerances upon request.
Delivery program from stock
- Thickness 3 - 20 mm
- Width 1000 - 2000* mm
- Length 2000 - 16000 mm
- Finish Black / Pickled & Oiled
* depending on thickness
A mill material certificate according to EN 10203:3.1 comes as default with deliveries of S700MC cut-to-length sheet.
Other certificates available upon request.